== Соединения Ti (том 33) ==
-
-

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

   
-

243. 33-0408
CrTiO3
Monoklin
Grupa 3

 Dexp     Dcal      d(D)      h    k    l     
3.6700   3.6694    .0006      1    1    0     
2.6800   2.6798    .0002      1    0    2     
2.5200   2.5203   -.0003      0    0    2     
2.2000   2.1997    .0003      1    2    0     
1.8350   1.8347    .0003      2    2    0     
1.6800   1.6802   -.0002      0    0    3     
1.4800   1.4795    .0005     -1    0    3    
1.4600   1.4601   -.0001      4    1    1     
1.3000   1.3013   -.0013      4    1    3
1.2600   1.2601   -.0001      0    0    4     
1.2200   1.2199    .0001      5    0    1     
1.1900   1.1900   -.0000      0    4    0     

a=6.1511 b= 4.7601 c= 5.382 beta= 69.46
da= .0002 db=.0002 dc=.002 dbeta=.02
V=     147.6

Triklin

 Dexp    Dcal     d(D)     h     k     l    
3.6700  3.6704  -.0004     1     0     0    
2.6800  2.6798   .0002     1     2     0    
2.5200  2.5196   .0004     1     2     1    
2.2000  2.2000   .0000     1     0     2    
1.8350  1.8351  -.0001     2     1     1    
1.6800  1.6802  -.0002     2     0     2    
1.4800  1.4800   .0000     0     4     2    
1.4600  1.4601  -.0001     1     4     2    
1.3000  1.2999   .0001     0     5     2    
1.2600  1.2598   .0002     2     4     2   
1.2200  1.2200  -.0000    -2    -1     2   
1.1900  1.1898   .0002    -3     2     0   

A=  3.8588  DA= .0003
B=  8.30281   DB= .00004
C=  4.6136  DC= .0004
GAMMA= 93.713 DGAMMA= .002
BETA = 72.256 DBETA = .002
ALPHA= 93.086 DALPHA= .003
V=     140.4

244. 33-0830
Li12Ti17O40
Rombik
Groupa 33,49,62

Dexp.   Dcal.    d(D)      h    k    l
4.4400  4.4365   .0035      1    1    0
3.4570  3.4566   .0004      1    2    0
2.6870  2.6869   .0001      1    3    0
2.4550  2.4555  -.0005      1    1    1
2.2430  2.2431  -.0001      1    2    1
2.1550  2.1554  -.0004      1    4    0
1.9860  1.9859   .0001      1    3    1
1.7730  1.7726   .0004      2    2    1
1.7280  1.7283  -.0003      2    4    0
1.6370  1.6372  -.0002      2    3    1
1.5270  1.5268   .0002      1    5    1
1.4740  1.4741  -.0001      0    0    2
1.3990  1.3989   .0001      1    1    2

a= 5.010  b= 9.550  c= 2.94826
da= .001  db= .001  dc= .00007
v= 141.06

245. 33-1081
Pr2Ti4{SO4}11
Triklin

  Dexp    Dcal     d(D)     h     k     l    
13.7000 13.6794   .0206     1     0     0    
9.5100  9.5024   .0076     0     1     0    
7.5600  7.5785  -.0185     0     0     1    
6.1600  6.1742  -.0142    -1     0     1    
5.6000  5.6048  -.0048     2     0     1    
4.5500  4.5598  -.0098     3     0     0   
4.5200  4.5169   .0031     0     2     1    
4.2700  4.2692   .0008    -2    -1     1    
3.7400  3.7367   .0033    -3     1     0   
3.6000  3.6006  -.0006     4     1     1    
3.4400  3.4407  -.0007    -1     1     2    
3.1890  3.1886   .0004     3     3     1     

    A= 14.70  DA= .01
B= 10.320 DB= .002
C=  8.057 DC= .002
GAMMA= 71.06 DGAMMA= .01
BETA = 75.05 DBETA = .02
ALPHA= 72.99 DALPHA= .02
V=    1087.7

246. 33-1113
Rb5HTi4O3F16
Rombik
Groupa 26,28,51

Dexp.   Dcal.    d(D)      h    k    l
3.4830  3.4837  -.0007      3    0    0
3.2480  3.2421   .0059      3    0    1
2.9430  2.9440  -.0010      0    1    0
2.3880  2.3872   .0008      1    1    2
2.2530  2.2529   .0001      3    0    3
2.1670  2.1671  -.0001      1    0    4

a=10.451  b= 2.944  c= 8.861
da= .001  db= .001  dc= .001
V= 272.6

247. 33-1154
Sm2Ti4{SO4}11
Triklin

 Dexp     Dcal      d(D)     h     k     l
4.2600   4.2707   -.0107     1    -1     1
3.7300   3.7300   -.0000     2     0     0
3.6000   3.6014   -.0014    -2     2     2
3.4100   3.4095    .0005     0    -1     2
3.2200   3.2179    .0021     0    -2     1
3.1800   3.1796    .0004     1    -2     1
3.1400   3.1400   -.0000    -3     1     1
3.0800   3.0810   -.0010    -3     2     2
2.7280   2.7284   -.0004    -3     1     0
2.5700   2.5702   -.0002     0     1     3
2.5310   2.5321   -.0011    -3     3     1
2.4290   2.4288    .0002    -4     2     2

A=  9.754  DA= .0029
B=  8.441  DB= .002
C=  9.5566 DC= .0005
GAMMA=120.603 DGAMMA= .007
BETA =122.651 DBETA = .006
ALPHA= 70.968 DALFA= .007
V=568.9

 

 

 

248. 33-1269
NaMnTi2O6
Triklin

 Dexp    Dcal     d(D)     h     k     l    
8.4100  8.4000   .0100     0     1     1    
7.2300  7.2371  -.0071     0    -1     1    
6.1200  6.1185   .0015     1     1     0    
5.4500  5.4487   .0013     1    -1     1    
4.8500  4.8458   .0042    -1     1     1    
4.5620  4.5557   .0063    -1     2     0   
4.0070  4.0025   .0045     1     2     2   
3.6290  3.6255   .0035     0    -3     1   
3.3290  3.3287   .0003     0     1     3   
3.0930  3.0947  -.0017     0     4     1   
3.0190  3.0185   .0005    -1    -2     2   
2.8390  2.8387   .0003     0    -4     1   

A=  7.1453 DA= .0009
B= 12.568  DB= .003
C= 10.370  DC= .002
GAMMA= 86.190 DGAMMA= .004
BETA = 75.824 DBETA = .004
ALPHA= 80.630 DALPHA= .002
V=     890.5

249. 33-1377
gamma-Ti{HPO4}2
Monoklin
Grupa 7,13

Dexp      Dcal       d(D)      h    k    l
9.2000    9.1620     .0380      0    1    0
5.2100    5.2064     .0036      1    1    0
4.4800    4.4776     .0024      0    1    1
3.4200    3.4176     .0024      0    2    1
3.1300    3.1272     .0028     -1    2    1
2.9900    2.9904    -.0004      2    1    0
2.7500    2.7504    -.0004      1    3    0
2.4100    2.4107    -.0007     -1    1    2
2.2900    2.2905    -.0005      0    4    0

  a= 6.3860 b= 9.1620 c=5.180 beta= 97.774
da= .0009 db=.0004 dc=.002 dbet=.005
V=     300.3

250. 33-1378
gamma-Ti{HPO4}2*H2O
Monoklin
Grupa  3

Dexp      Dcal       d(D)      h    k    l
11.4700   11.5600    -.0900      0    1    0
5.4800    5.5054    -.0254      1    1    0
3.8500    3.8501    -.0001     -1    0    1
3.7900    3.7936    -.0036      0    1    1
3.6600    3.6528     .0072     -1    1    1
3.2800    3.2816    -.0016      1    3    0
3.1300    3.1305    -.0005      2    0    0
3.0500    3.0491     .0009      1    0    1
2.8900    2.8900     .0000      0    4    0

a=  6.470 b= 11.5600 c=4.150 beta= 104.594
da= .001 db=.0002 dc=.005 dbet=.002
V=     300.4

251. 33-1382
TiP2
Triklin

Dexp     Dcal      d(D)     h     k     l
3.8400   3.8404   -.0004    -1     1     2
3.4200   3.4209   -.0009    -1    -1     2
3.0400   3.0408   -.0008    -2     0     2
2.7500   2.7511   -.0011    -2    -1     2
2.6200   2.6200    .0000    -1     0     3
2.4800   2.4792    .0008    -2     1     3
2.3700   2.3684    .0016    -1    -3     2
2.2400   2.2401   -.0001    -3     0     2
2.1900   2.1897    .0003     2    -3     1
2.1600   2.1588    .0012     0     4     2
1.9900   1.9898    .0002     3     1     0
1.9480   1.9481   -.0001     2     1     2

    A=  7.0483 DA= .0008
B= 10.614  DB= .001
C=  7.9441 DC= .0006
GAMMA=103.216 DGAMMA= .009
BETA =114.272 DBETA = .008
ALPHA= 81.685 DALPHA= .003
V=526.5

252. 33-1383
Ti{SeO3}2
Monoklin
Grupa         14

Dexp      Dcal       d(D)      h    k    l
3.9100    3.9094     .0006      2    1    0
3.4400    3.4411    -.0011      0    2    1
3.1600    3.1599     .0001      0    0    2
3.0100    3.0111    -.0011     -2    2    1
2.9500    2.9488     .0012      0    1    2
2.5100    2.5101    -.0001      0    3    1
2.1400    2.1400    -.0000     -4    1    2
2.0400    2.0404    -.0004      0    1    3
1.9550    1.9547     .0003      4    2    0
1.8660    1.8659     .0001     -3    2    3
1.7270    1.7267     .0003     -2    3    3
1.5560    1.5561    -.0001     -5    3    1

a= 9.4846 b= 8.2051 c= 6.7400 beta= 110.335
da= .0008 db=.0002 dc=.0006 dbet= .001
V=     491.8

253 33-1395
Tb2TiO5
Monoklin
Grupa 4,11

Dexp      Dcal       d(D)      h    k    l
5.2000    5.2055    -.0055      0    2    0
4.9500    4.9471     .0029      0    1    2
4.7200    4.7239    -.0039      0    2    1
3.8200    3.8184     .0016      1    1    2
2.5300    2.5305    -.0005     -2    2    2
3.3500    3.3482     .0018     -1    0    3
3.3200    3.3160     .0040      0    3    1
3.0400    3.0339     .0061     -2    1    1
2.9800    2.9768     .0032     -1    3    1
2.9500    2.9531    -.0031      0    3    2
2.9300    2.9311    -.0011      2    1    1
2.6500    2.6501    -.0001      1    3    2

  a= 6.4920 b= 10.411 c= 11.273 beta= 94.044
da= .0001 db=.001 dc= .001 dbet=.002
V=     760.0

254. 33-1914
C38H30Ti
Rombik
Groupa 26,28,51

Dexp.   Dcal.    d(D)      h    k    l
9.2000  9.2500  -.0500      1    0    0
7.8000  7.7408   .0592      1    0    1
5.5000  5.4720   .0280      1    1    0
5.1000  5.1032  -.0032      1    1    1
4.9000  4.8961   .0039      0    1    2
4.2000  4.1996   .0004      1    0    3

a= 9.250  b= 6.787  c=14.140
da= .001  db= .001  dc= .001
v= 887.7

 
 
-
 
-