== Соединения Fe (томa 47-50) ==
-
-

 

   
-

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

1. 47-0698
Fe0.0132SiO2.0198
Triklin

  Dexp     Dcal      d(D)     h     k     l
11.0510  11.1056   -.0546    -1     0     1
9.9356   9.9465   -.0109     1     1     0
9.7177   9.7074    .0103     1     0     1
7.4057   7.4138   -.0081     0     1     1
7.0530   7.0616   -.0086    -1     1     1
6.6819   6.6885   -.0066    -1    -1     2
6.3481   6.3431    .0050     0     0     2
6.0056   6.0074   -.0018     0     2     0
5.6984   5.6992   -.0008     1    -2     0
5.5564   5.5596   -.0032     0    -2     2
4.9967   4.9963    .0004     3    -1     1
4.5870   4.5849    .0021     1     1     2

A= 18.04  DA= .02
B= 13.04  DB= .01
C= 13.907 DC= .003
GAMMA= 86.81  DGAMMA= .03
BETA = 98.74  DBETA = .07
ALPHA=112.87  DALPHA= .04
V=2975

2. 47-1398
Ca3Fe4O4S3
Triklin

 Dexp     Dcal      d(D)     h     k     l
7.4500   7.4959   -.0459     0     1     1
4.8000   4.7999    .0001     0    -1     1
4.3900   4.3925   -.0025     2     0     0
3.8800   3.8814   -.0014     0     2     0
3.7500   3.7480    .0020     0     2     2
3.6800   3.6808   -.0008    -2     0     1
3.5900   3.5924   -.0024     2     1     1
3.4400   3.4450   -.0050     2     1     0
3.0500   3.0529   -.0029    -2     2     2
2.9000   2.8983    .0017    -2    -1     1
2.7900   2.7891    .0009     0     3     2
2.7700   2.7702   -.0002     2     2     1

A=  9.131 DA= .002
B=  8.79250   DB= .00004
C=  9.3176  DC= .0003
GAMMA=103.40  DGAMMA= .01
BETA = 87.734  DBETA = .009
ALPHA= 66.4899 DALPHA= .0003
V=659.2

3. 47-1640
Al65Cu20Fe12Mn3
Tetrag.
Grupa  75

Dexp.    Dcal.     d(D)       h     k     l    
2.1198   2.1201   -.0003       2     2     1    
2.0112   2.0115   -.0003       3     0     1    
1.4601   1.4600    .0001       3     3     1    
1.4244   1.4238    .0006       4     2     0    
1.2444   1.2444    .0000       4     1     3    

a=   6.367 c=   6.304
da= .001  dc= .002
v=    255.6

4. 47-1641
Al65Cu20Fe9Mn6
Rombik
Groupa 56

Dexp.   Dcal.    d(D)      h    k    l
2.1234  2.1235  -.0001      3    1    0
2.0164  2.0162   .0002      1    3    0
1.4612  1.4608   .0004      0    3    2
1.4279  1.4279   .0000      1    3    2
1.2471  1.2472  -.0001      0    4    2

a= 6.761  b= 6.337  c= 4.045
da= .001  db= .001  dc= .001
v= 173.3

5. 47-1642
Al65Cu20Fe6Mn9
Tetragon
Groupa 141

Dexp.   Dcal.    d(D)      h    k    l

2.1313  2.1315  -.0002      2    1    1
2.0229  2.0244  -.0015      2    2    0
1.4676  1.4678  -.0002      3    2    1
1.4319  1.4314   .0005      4    0    0
1.2511  1.2511   .0000      1    0    3

a= 5.726  c=   3.846
da= .002  dc= .003
V= 126.1

6. 47-1643
Al65Fe20W15
Rombik
Groupa 30,53

Dexp.   Dcal.    d(D)      h    k    l
3.8400  3.8440  -.0040      1    0    0
3.4000  3.3970   .0030      1    1    0
2.1600  2.1599   .0001      1    0    2
2.0500  2.0476   .0024      1    3    0
1.4900  1.4900  -.0000      0    4    2

a= 3.844  b= 7.258  c= 5.222
da= .001  db= .002  dc= .001
V= 145.7

7. 47-2018
C34H40FeN10
Triklin

 Dexp     Dcal      d(D)     h     k     l
6.7220   6.7069    .0151     0     0     1
5.8920   5.9150   -.0230     0    -2     1
5.6910   5.6836    .0074     1     1     0
5.5040   5.5052   -.0012    -1     1     0
5.1660   5.1579    .0081     1     2     0
5.0120   5.0374   -.0254     0    -3     1
4.9030   4.8990    .0040    -1     2     0
4.2070   4.2059    .0011    -1    -3     1
4.0520   4.0522   -.0002     1     0     1
3.9580   3.9602   -.0022     0     5     0
3.7020   3.7034   -.0014     1     2     1
3.6250   3.6187    .0063     0    -5     1

A=  5.94821   DA= .00009
B= 20.0365   DB= .007
C=  6.8881  DC= .0005
GAMMA= 85.19 DGAMMA= .02
BETA =100.968 DBETA = .001
ALPHA= 98.12 DALPHA= .01
V=2022

8. 47-2019
C34H40FeN10*2H2O
Triklin

 Dexp     Dcal      d(D)     h     k     l
8.7640   8.7548    .0092    -1     1     1
8.3240   8.3370   -.0130    -1    -1     1
7.9250   7.9614   -.0364     1     1     0
7.1560   7.1555    .0005    -1     0     2
6.6550   6.6552   -.0002    -2     0     1
6.4000   6.3875    .0125     0     0     2
6.1070   6.1057    .0013    -1     1     2
5.8910   5.8887    .0023    -2     0     2
5.6910   5.6957   -.0047    -2     1     0
5.5960   5.5990   -.0030    -1     2     1
5.1260   5.1167    .0093     1    -2     1
5.0500   5.0423    .0077     2     1     0

A= 13.40 DA= .01
B= 12.565 DB= .002
C= 14.389 DC= .008
GAMMA= 96.71 DGAMMA= .02
BETA =116.66 DBETA = .05
ALPHA= 92.87 DALPHA= .01
V=2135

9. 47-2020
C34H40FeN10O4
Triklin

Dexp     Dcal      d(D)     h     k     l
6.7230   6.7184    .0046     2     2     0
5.9970   5.9995   -.0025    -1     0     1
5.7400   5.7446   -.0046    -1     1     1
5.4600   5.4636   -.0036     1     3     1
5.1260   5.1201    .0059    -2     2     0
4.9750   4.9824   -.0074     2    -1     1
4.8330   4.8358   -.0028     1     4     0
4.6980   4.6974    .0006    -2     0     1
4.5110   4.5033    .0077     1     4     1
4.3660   4.3614    .0046     0    -3     1
3.7630   3.7616    .0014     2     5     0
3.4790   3.4799   -.0009     2     0     2

A= 15.6997  DA= .0005
B= 19.852   DB= .005
C=  7.462  DC= .001
GAMMA= 71.85 DGAMMA= .01
BETA = 76.00   DBETA = .02
ALPHA= 77.28 DALPHA= .04
V=2118

10. 47-2045
C12H11FeO6P2*H2O
Rombik
Groupa 16

Dexp.   Dcal.    d(D)      h    k    l
15.1100 15.1054   .0046      1    0    0
7.5600  7.5527   .0073      2    0    0
5.0400  5.0351   .0049      3    0    0
4.7000  4.7058  -.0058      3    0    1
4.4100  4.4095   .0005      0    0    3
3.9200  3.9200   .0000      0    1    0
3.7800  3.7764   .0036      4    0    0
3.0200  3.0211  -.0011      5    0    0

a=15.105  b= 3.920  c=13.2284
da= .004  db= .004  dc= .0007
V= 783.3

1. 48-1410
Fe3Tl5S7
Rombik
Groupa 34,58

Dexp.   Dcal.    d(D)      h    k    l
3.6800  3.6812  -.0012      1    2    0
3.4900  3.4909  -.0009      1    1    2
3.3360  3.3301   .0059      0    2    2
3.0510  3.0435   .0075      2    0    0
2.9200  2.9215  -.0015      1    2    2
2.8900  2.8909  -.0009      2    1    0
2.8340  2.8333   .0007      1    0    3
2.7640  2.7682  -.0042      2    1    1
2.7080  2.7089  -.0009      1    1    3

a= 6.087  b= 9.245  c= 9.6035
da= .001  db= .004  dc= .0008
V= 540.4

2. 48-1411
Fe2Tl4S5
Monoklin
Grupa 3

 Dexp     Dcal      d(D)      h    k    l     
4.0800   4.0792    .0008     -2    1    1     
3.5560   3.5555    .0005      0    3    0     
3.3440   3.3440    .0000     -2    0    2     
3.0930   3.0942   -.0012      2    2    1     
2.9110   2.9096    .0014      1    2    2     
2.8440   2.8433    .0007      2    3    0     
2.6950   2.6947    .0003     -3    2    1     
2.5290   2.5292   -.0002      0    4    1     
2.1670   2.1672   -.0002      2    0    3     
1.8600   1.8601   -.0001      2    5    1     
1.8360   1.8363   -.0003     -5    0    2    

a=9.611 b=10.6666 c= 8.097 beta= 99.78
da=.008 db= .0004 dc=.005 dbeta=.09
V=818.0

3. 48-1412
FeTl14S10
Monoklin
GRUPA  3,6,10

Dexp.    Dcal.     d(D)      h    k    l
3.4670   3.4659    .0011     -1    1    1
3.2710   3.2714   -.0004      2    0    1
3.2080   3.2079    .0001      1    1    1
2.9720   2.9713    .0007     -1    1    2
2.6320   2.6321   -.0001      2    0    2
2.5430   2.5439   -.0009      2    1    1
2.1890   2.1888    .0002     -2    0    4
2.0110   2.0110    .0000     -1    1    4
1.9290   1.9290    .0000      4    0    0

a= 7.952 b=4.0460 c= 9.2824 beta=104.00
da=.0073 db=.0001 dc=.0007 dbet=.01
V=289.7

4. 48-1413
Fe2Tl3S4
Rombik
Groupa 34,58

Dexp.   Dcal.    d(D)      h    k    l
3.6900  3.6916  -.0016      0    2    0
3.4920  3.4938  -.0018      3    0    1
3.4040  3.4072  -.0032      1    0    3
3.3340  3.3299   .0041      1    2    1
3.3060  3.3041   .0019      3    1    0
3.1560  3.1580  -.0020      3    1    1
2.9330  2.9338  -.0008      1    2    2
2.7850  2.7853  -.0003      2    1    3
2.6110  2.6114  -.0004      3    2    0
2.5360  2.5375  -.0015      3    2    1
2.5050  2.5038   .0012      1    2    3
2.4640  2.4626   .0014      4    0    2

a=11.084  b= 7.383  c=10.742
da= .007  db= .005  dc= .008
V= 879

5. 48-1114
Fe4Tl3S6
Geksagon
Groupa 186,190,194

Dexp.   Dcal.    d(D)      h    k    l
4.1600  4.1556   .0044      1    0    1
3.3200  3.3203  -.0003      3    0    0
2.9040  2.9065  -.0025      2    1    1
2.6850  2.6867  -.0017      3    0    1
2.4360  2.4342   .0018      2    2    1

a= 11.502 c=4.572
da= .005 dc=.001
v= 523.9

6. 48-1932
СC12H15FeN*5.26TaS2*2.63H2O
Tetragon
Groupa 85,118,129

Dexp.   Dcal.    d(D)      h    k    l
11.9940 11.9128   .0812      0    0    1
6.0015  5.9564   .0451      0    0    2
3.9917  3.9881   .0036      1    0    1
2.9902  2.9927  -.0025      1    1    0
2.3884  2.3900  -.0016      1    1    3
1.9876  1.9855   .0021      0    0    6
1.7024  1.7018   .0006      0    0    7
1.4890  1.4891  -.0001      0    0    8
1.3234  1.3236  -.0002      0    0    9
1.1912  1.1913  -.0001      0    0   10
1.0921  1.0921   .0000      3    2    4

a=   4.232  c=  11.913
da= .002  dc= .004
V= 213.4

7. 48-1978
C16H13ClFeN4O8S2*3H2O
Rombik
Groupa 31,59

Dexp.   Dcal.    d(D)      h    k    l
7.5360  7.5179   .0181      2    0    0
4.7090  4.7086   .0004      3    0    1
4.4010  4.3819   .0191      1    0    3
4.0400  4.0492  -.0092      3    0    2
3.6330  3.6258   .0072      4    0    1
3.4660  3.4703  -.0043      1    1    0
3.3760  3.3813  -.0053      3    0    3
3.1000  3.0977   .0023      1    1    2
2.4650  2.4653  -.0003      6    0    1
2.2900  2.2904  -.0004      0    0    6
2.0670  2.0668   .0002      4    1    4

a=15.036  b= 3.567  c=13.742
da= .002  db= .002  dc= .009
V= 736.9

1. 49-0719
K0.96Fe0.22Mg0.64Al3.45Si7.69O20{OH}4*xH2O
Geksagon
Grupa  143

Dexp.   Dcal.    d(D)      h    k    l
11.5620 11.5240   .0380      1    0    0
4.9400  4.9021   .0379      0    0    1
3.2560  3.2560  -.0000      2    1    1
2.5190  2.5147   .0043      4    1    0
2.0180  2.0206  -.0026      3    3    1
1.4080  1.4079   .0001      7    2    0

a= 13.31 c= 4.902054
da= .01  dc=.05
V= 752

2. 49-1076
C4H3Fe2O11Zn*4H2O
Triklin

 Dexp     Dcal      d(D)     h     k     l
4.7590   4.7570    .0020     0     1     2
4.6550   4.6448    .0102     1     0     0
3.9050   3.9092   -.0042     0    -1     2
3.6730   3.6724    .0006    -1     2     2
3.5550   3.5553   -.0003     0     2     2
2.9490   2.9484    .0006     1     0     2
2.7040   2.7053   -.0013     0     3     0
2.6490   2.6468    .0022    -1     2     4
2.6280   2.6316   -.0036     0     3     2
2.5570   2.5610   -.0040     0     1     4
2.5120   2.5116    .0004     0     0     4
2.2290   2.2281    .0009    -2     2     4

A=  5.1898 DA= .0001
B=  8.7390 DB= .0003
C= 11.242  DC= .001
GAMMA=107.97  DGAMMA= .01
BETA =113.751 DBETA = .006
ALPHA= 71.782 DALPHA= .001
V=433.6

3. 49-0138
FeTl5S4
Triklin

Dexp     Dcal      d(D)     h     k     l
3.7860   3.7858    .0002     0     1     1
3.6980   3.6957    .0023     0    -1     1
3.6040   3.6031    .0009     1     1     0
3.4790   3.4779    .0011     0    -2     1
3.4130   3.4166   -.0036     1     2     0
3.3250   3.3318   -.0068     1    -1     1
3.2440   3.2382    .0058     1     2     1
3.1890   3.1841    .0049     1    -2     1
3.1130   3.1116    .0014     0     4     1
2.9960   2.9991   -.0031    -1     4     0
2.9800   2.9836   -.0036     1    -3     1
2.8310   2.8311   -.0001     0     5     1

A=  4.00784   DA= .00002
B= 19.73639   DB= .00008
C=  4.14665   DC= .00008
GAMMA= 90.4788 DGAMMA= .0002
BETA = 67.0115 DBETA = .0006
ALPHA= 86.7842 DALPHA= .0003
V=301.3

4. 49-1529
{N2H5}2FeF5
Triklin

 Dexp    Dcal     d(D)     h     k     l    
7.1200  7.1311  -.0111     0     1     1    
6.4300  6.4338  -.0038     0    -1     1    
5.8000  5.8016  -.0016    -1     0     1    
5.2200  5.2191   .0009    -1     2     0    
4.0800  4.0805  -.0005    -1    -2     1    
3.9100  3.9107  -.0007     0     0     2    
3.6900  3.6880   .0020     1     3     0    
3.5500  3.5541  -.0041    -2     0     1    
3.4600  3.4556   .0044    -1     2     2    
3.3400  3.3381   .0019    -2     2     1    
3.2000  3.1960   .0040     2     0     1    
3.1200  3.1224  -.0024    -1     4     1    

A=  7.558  DA= .002
B= 13.578  DB= .004
C=  7.965  DC= .001
GAMMA= 96.17 DGAMMA= .01
BETA = 98.55 DBETA = .01
ALPHA= 82.43 DALPHA= .01
V=     797.98

5. 49-1555
Ca2Fe2O5.12
Triklin

 Dexp    Dcal     d(D)     h     k     l    
3.8580  3.8559   .0021    -1     0     1    
3.7310  3.7333  -.0023     1     1     0    
2.7630  2.7633  -.0003    -1    -2     1    
2.6810  2.6815  -.0005     1     2     0    
2.6370  2.6368   .0002     0     2     1    
2.5430  2.5429   .0001    -1    -2     2    
2.4580  2.4580  -.0000    -1     1     2    
2.2060  2.2060  -.0000     0     2     2    
2.1810  2.1815  -.0005    -1    -2     3    
1.9290  1.9287   .0003    -2    -2     1    
1.8660  1.8667  -.0007     2     2     0    
1.7450  1.7449   .0001    -2     0     3    

A=  4.223   DA= .001
B=  6.2026  DB= .0001
C=  8.212   DC= .005
GAMMA= 75.534 DGAMMA= .001
BETA =101.77  DBETA = .04
ALPHA=101.92  DALPHA= .01
V=     201.1

6. 49-1609
Al64.3Cu23.5Fe12.2
Triklin

  Dexp     Dcal      d(D)     h     k     l
15.5500  15.5689   -.0189     0     0     1
10.4540  10.4812   -.0271     1     0     0
5.6010   5.6033   -.0023     1     1     1
5.2460   5.2464   -.0004    -1    -1     1
3.7740   3.7745   -.0005    -2     1     0
3.7340   3.7340   -.0000    -2     1     1
3.4940   3.4937    .0003     3     0     0
3.4030   3.4019    .0011     3     0     1
3.3000   3.2989    .0011     2    -1     2
3.2490   3.2500   -.0010    -1     1     4
3.2020   3.1991    .0029    -3     0     2
2.8940   2.8927    .0013     2     2     1

A= 10.5891   DA= .0002
B=  6.4111   DB= .0008
C= 15.675   DC= .002
GAMMA= 81.838 DGAMMA= .005
BETA = 89.614 DBETA = .002
ALPHA= 83.370 DALPHA= .003
V=1045.5

7. 49-1730
Al60Cu30Fe10
Triklin

Dexp     Dcal      d(D)     h     k     l
16.9640  17.0092   -.0452     0     0     1
9.0690   9.0644    .0046     0     1     0
5.6450   5.6456   -.0006     0    -1     2
5.5090   5.5095   -.0005    -1    -1     1
3.7480   3.7480    .0000     2    -1     2
3.6950   3.6944    .0006     0    -2     2
3.4150   3.4157   -.0007    -2    -1     2
3.3810   3.3824   -.0014    -2     2     0
3.2550   3.2561   -.0011     1     0     5
3.2420   3.2421   -.0001     1     1     5
3.2240   3.2241   -.0001     2     0     4
2.1110   2.1109    .0001    -4     1     3

A=  9.26214   DA= .00001
B=  9.2928   DB= .0004
C= 17.4033   DC= .0001
GAMMA= 94.392 DGAMMA= .002
BETA = 87.5117 DBETA = .0001
ALPHA= 78.284 DALPHA= .005
V=1459.6

8. 49-2177
C4H4FeO5
Triklin

 Dexp    Dcal     d(D)     h     k     l    
4.0200  4.0220  -.0020     0     1     1    
3.8600  3.8602  -.0002     0    -1     1    
3.5200  3.5205  -.0005    -1     1     0     
3.3000  3.2997   .0003     1     1     0    
2.8700  2.8687   .0013    -1     1     1    
2.8100  2.8117  -.0017     0     1     2    
2.5200  2.5210  -.0010     2     0     1    
2.3400  2.3402  -.0002     2     0     2    
2.2600  2.2598   .0002     0    -2     1    
2.1200  2.1187   .0013     1     1     3   
1.9300  1.9301  -.0001     0    -2     2   
1.7700  1.7701  -.0001     1     0     4   
1.6800  1.6803  -.0003     0     2     3   
1.6300  1.6299   .0001    -2     1     2   
1.5700  1.5700   .0000    -1     3     0   

A=  5.051 DA= .002
B=  4.8897 DB= .0006
C=  7.083  DC= .001
GAMMA= 93.07 DGAMMA= .02
BETA = 70.618 DBETA = .003
ALPHA= 88.70  DALPHA= .02
V=     164.6

9. 49-2178
C4H4FeO5
Triklin

Dexp     Dcal      d(D)     h     k     l
4.1000   4.1019   -.0019     2     0     0
3.5400   3.5399    .0001     0     2     0
3.3200   3.3162    .0038     0     2     2
2.9300   2.9226    .0074     1     2     0
2.8300   2.8238    .0062     3     0     1
2.5100   2.5084    .0016     1     0     3
2.4100   2.4103   -.0003    -2     0     2
2.3300   2.3309   -.0009     2     2     0
2.2400   2.2407   -.0007     2    -2     2
2.1500   2.1493    .0007     1    -1     3
2.0000   2.0001   -.0001    -3    -1     1
1.8600   1.8602   -.0002    -2     4     0

A=  8.786 DA= .008
B=  8.030 DB= .001
C=  8.073 DC= .003
GAMMA=104.05 DGAMMA= .01
BETA = 80.9430 DBETA = .0009
ALPHA= 68.82 DALPHA= .03
V=495.6

1. 50-1463
Tm30Fe5Si65
Triklin

 Dexp     Dcal      d(D)     h     k     l
3.9489   3.9464    .0025     1     0     0
3.5854   3.5870   -.0016     1     1     1
3.3719   3.3710    .0009     0    -3     1
2.9833   2.9917   -.0084     0     4     0
2.8686   2.8680    .0006     0     0     2
2.7472   2.7447    .0025     1    -3     1
2.6502   2.6489    .0013     0    -2     2
2.4877   2.4872    .0005     1    -2     2
2.2894   2.2859    .0035    -1     3     1
2.0267   2.0264    .0003    -1     4     1
1.9932   1.9928    .0004    -1    -2     2
1.9105   1.9120   -.0015     0     0     3

A=  4.102 DA= .001
B= 11.991 DB= .001
C=  5.970 DC= .001
GAMMA= 88.82 DGAMMA= .03
BETA = 74.28 DBETA = .01
ALPHA= 92.99 DALPHA= .01
V=282.2

2. 50-1464
Tm37Fe25Si38
Triklin

Dexp     Dcal      d(D)     h     k     l
3.7853   3.7834    .0019     2    -3     1
3.6439   3.6432    .0007     2     1     1
3.3922   3.3955   -.0033    -2     1     1
3.3692   3.3685    .0007     0     4     0
2.8245   2.8258   -.0013     0    -2     2
2.5849   2.5847    .0002    -3     2     1
2.5450   2.5451   -.0001     1     4     1
2.5164   2.5166   -.0002    -1    -2     2
2.5162   2.5159    .0003     0     2     2
2.4524   2.4532   -.0008     4     0     0
2.3910   2.3908    .0002     0    -4     2

A= 10.553 DA= .001
B= 14.3863 DB= .0005
C=  6.0592 DC= .0003
GAMMA=108.431  DGAMMA= .005
BETA = 75.226  DBETA = .004
ALPHA=103.127  DALPHA= .008
V=833.0

3. 50-1465
Tm40Fe19Si41
Triklin

 Dexp     Dcal      d(D)     h     k     l
3.7826   3.7821    .0005     0     0     2
3.2931   3.2923    .0008    -3     1     0
3.1745   3.1755   -.0010    -1    -1     2
3.0088   3.0078    .0010    -3     0     1
2.6314   2.6314   -.0000     3    -1     2
2.6205   2.6207   -.0002     2    -2     2
2.4872   2.4872   -.0000     4     0     0
2.3039   2.3038    .0002    -1     2     2
2.2286   2.2285    .0001    -1     3     0
2.1552   2.1553   -.0001     4     1     0
2.1483   2.1482    .0001     1     1     3
2.0739   2.0739   -.0000     3    -3     1
1.7778   1.7778   -.0000     4     2     0
1.7019   1.7020   -.0001    -3     2     3
1.5878   1.5878    .0000    -2    -2     4

A= 10.2765  DA= .0003
B=  6.7948  DB= .0005
C=  7.6886  DC= .0004
GAMMA=104.434 DGAMMA= .001
BETA = 86.012 DBETA = .002
ALPHA=100.213 DALPHA= .002
V=511.5

4. 50-2249
{C10H8Fe*0.85C12H4N4}n
Rombik
Grupa 16

Dexp.    Dcal.     d(D)      h    k    l     
7.4400   7.4820    .0420      1    0    0     
6.5500   6.5617    .0117      1    0    1     
5.8300   5.8052   -.0248      1    1    0     
5.0500   5.0436   -.0064      1    0    2     
3.9200   3.9192   -.0008      1    2    0     
3.5800   3.5821    .0021      1    1    3     
3.4200   3.4141   -.0059      0    0    4    
3.2000   3.2009    .0009      0    1    4    

a= 7.482 b= 9.20 c= 13.656
da=.009 db=.01 dc=.005
V=     940

5. 50-2250
{C10H8Fe*0.83C12H4N4}n
Rombik
Groupa         19

 Dexp.   Dcal.    d(D)      h    k    l
7.4000  7.3813   .0187      0    0    1
6.5500  6.5181   .0319      1    0    1
5.8100  5.7899   .0201      1    1    0
5.0600  5.0581   .0019      2    0    1
3.9200  3.9223  -.0023      3    0    1
3.5700  3.5669   .0031      1    0    2
3.1900  3.1848   .0052      0    2    0

a=13.89  b= 6.37  c= 7.38
da= .01  db= .05  dc= .01

6. 50-2251
{C10H8Fe*0.80C12H4N4}n
Rombik
Groupa  19

Dexp.   Dcal.    d(D)      h    k    l
8.1800  8.1714   .0086      1    1    0
5.0900  5.1056  -.0156      0    2    0
4.7900  4.7810   .0090      1    2    0
3.6800  3.6847  -.0047      0    0    1
3.4700  3.4659   .0041      0    1    1
3.3600  3.3590   .0010      1    1    1
3.2400  3.2411  -.0011      2    0    1

a=13.63  b=10.21  c= 3.6847
da= .01  db= .02  dc= .0006
V= 513

 
     
-
     
-