== Соединения Zn (томa 37-39) ==
-
-

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

 

O

   
-

422. 37-0113
BaZnGeO4
Monoklin
Grupa  3
 
 Dexp     Dcal       d(D)       h    k    l     
4.6790   4.6725    .0065      1    0    1     
3.8000   3.8010   -.0010      1    1    0     
3.1730   3.1726    .0004      1    1    1     
2.7100   2.7102   -.0002     -3    0    1     
2.6820   2.6818    .0002      0    1    2     
2.6630   2.6627    .0003      3    0    0     
2.1610   2.1608    .0002      0    2    0     
2.0550   2.0552   -.0002      2    1    2     
2.0310   2.0308    .0002     -1    2    1     
1.9610   1.9612   -.0002      1    2    1     
 
a=   8.227 b=  4.3216 c= 7.045 beta= 103.84
da=  .003 db= .0008 dc=.004 dbeta=.01
V=     243.2

423. 37-0193
Mn3Zn{PO4}2*2H2O
Geksagon

Dexp.   Dcal.    d(D)      h    k    l
7.9500  7.9726  -.0226      0    0    1
3.9900  3.9863   .0037      0    0    2
2.9610  2.9632  -.0022      1    1    2
1.9600  1.9593   .0007      2    1    3
1.5720  1.5722  -.0002      3    0    4

a=  8.860 c= 7.973
da= .008 dc=.002
V= 542.0

424. 37-0194
gamma-MnZn{PO4}2
Triklin

  Dexp     Dcal      d(D)     h     k     l
4.3400   4.3397    .0003     0    -2     2
4.0400   4.0412   -.0012     2     0     0
3.8800   3.8803   -.0003     0    -3     1
3.7200   3.7196    .0004     2     1     1
3.4400   3.4415   -.0015     1    -3     2
3.2500   3.2488    .0012     1    -2     3
3.0530   3.0522    .0008    -2     1     1
2.9380   2.9389   -.0009     1    -3     3
2.8260   2.8266   -.0006     0    -4     2
2.7530   2.7519    .0011     3    -1     1
2.6620   2.6640   -.0020    -2     0     2
2.5240   2.5233    .0007    -1     4     0

A=  8.4173  DA= .0003
B= 11.664  DB= .001
C= 10.0728  DC= .0003
GAMMA= 93.144  DGAMMA= .003
BETA = 74.068 DBETA = .007
ALPHA=111.849 DALPHA= .009
V=881.4

425. 37-0195
beta-Mn2Zn{PO4}2
Triklin

   Dexp     Dcal      d(D)     h     k     l
3.8600   3.8563    .0037    -1    -1     1
3.5900   3.5873    .0027     2     0     2
3.4800   3.4822   -.0022    -2     1     0
3.1620   3.1653   -.0033     2     1     0
3.0560   3.0563   -.0003     2    -2     2
2.9190   2.9189    .0001    -2     0     1
2.8740   2.8743   -.0003     0    -2     2
2.8440   2.8454   -.0014     0     1     2
2.7090   2.7084    .0006     1     0     3
2.5880   2.5876    .0004     1    -2     3
2.4150   2.4166   -.0016     3     1     1
2.3170   2.3159    .0011     1    -3     1

A=  9.0244   DA= .0002
B=  7.0166   DB= .0003
C=  8.9107   DC= .0002
GAMMA=106.395  DGAMMA= .001
BETA = 59.4783  DBETA = .0004
ALPHA=112.771  DALPHA= .002
V=445.5

426. 37-0382
Li3Zn9{PO4}7
Triklin

Dexp     Dcal      d(D)     h     k     l
5.0220   5.0218    .0002    -1    -1     1
4.3010   4.2995    .0015     0    -2     1
4.0580   4.0599   -.0019     0     0     2
3.9940   3.9952   -.0012    -2     0     1
3.5550   3.5557   -.0007    -1    -1     2
3.4050   3.4054   -.0004    -2    -1     1
3.2130   3.2159   -.0029     0    -3     1
3.1970   3.1976   -.0006     1     0     2
3.1350   3.1372   -.0022    -2     3     0
3.0710   3.0717   -.0007     1    -3     1
2.9420   2.9416    .0004    -2    -1     2
2.8220   2.8258   -.0038    -2    -2     1

A=  8.616   DA= .008
B= 12.3315  DB= .0006
C=  8.949   DC= .006
GAMMA=109.94  DGAMMA= .02
BETA =112.55  DBETA = .06
ALPHA= 72.97  DALPHA= .01
V=811.1

427. 37-0408
Na2ZnSiO4
Triklin

Dexp     Dcal      d(D)     h     k     l
4.2900   4.2928   -.0028     0     1     2
4.2390   4.2397   -.0007     2     1     0
4.2080   4.2072    .0008     2     0     0
3.7620   3.7612    .0008    -1     0     2
3.7040   3.7016    .0024    -2     1     0
3.6080   3.6151   -.0071    -2    -1     1
3.5440   3.5474   -.0034    -1     1     2
3.3570   3.3594   -.0024     2     1     2
2.9550   2.9548    .0002     1     1     3
2.9360   2.9346    .0014     1     0     3
2.8590   2.8594   -.0004    -2    -1     2
2.7070   2.7082   -.0012    -1     0     3

A=  8.69599   DA= .00004
B= 11.63978   DB= .00004
C=  9.09351   DC= .00001
GAMMA= 77.3017 DGAMMA= .0001
BETA = 81.4713  DBETA = .0002
ALPHA= 83.3973  DALPHA= .0001
V=884.3

428. 37-0653
ZnBr2*2H2O
Rombik
Groupa   29,57

Dexp.   Dcal.    d(D)      h    k    l
6.3000  6.3032  -.0032      1    2    0
4.0060  4.0071  -.0011      3    1    0
3.9780  3.9879  -.0099      2    2    1
3.6780  3.6746   .0034      0    0    2
3.5050  3.5032   .0018      1    4    0
3.1520  3.1516   .0004      2    4    0
2.7100  2.7082   .0018      3    1    2
2.5890  2.5894  -.0004      0    4    2
2.5340  2.5356  -.0016      1    4    2
2.0857  2.0854   .0003      0    7    0

a=12.501  b=14.598  c= 7.349
da= .007  db= .005  dc= .005
V=1341

429. 37-0665
C4O9TiZn*2.5H2O
Monoklin
Grupa 3

Dexp     Dcal      d(D)      h    k    l   
4.6430   4.6413    .0017      1    1    0     
3.8840   3.8836    .0004      3    0    1     
3.5240   3.5257   -.0017     -3    0    1     
2.9330   2.9331   -.0001      3    1    2     
2.6800   2.6795    .0005      3    1    3     
2.6200   2.6202   -.0002      4    0    3     
2.5340   2.5339    .0001      0    2    0     
2.3280   2.3275    .0005      4    1    3     
2.2090   2.2092   -.0002     -5    0    1     
2.1390   2.1394   -.0004      2    0    6     
2.0690   2.0685    .0005      6    0    3
2.0210   2.0208    .0002      5    1    3     

a= 11.7422 b=  5.0678 c=  13.0880 beta= 79.88
da= .0006 db=.0005 dc= .004 dbeta=.01
V=     766.7

430. 37-1119
InZnCl4
Triklin

Dexp     Dcal      d(D)      h     k     l
4.2600   4.2651   -.0051     2     0     0
4.0300   4.0318   -.0018     0     1     1
3.8700   3.8592    .0108    -2    -1     1
3.7800   3.7735    .0065     0    -1     2
3.6500   3.6508   -.0008     2     1     0
3.5700   3.5726   -.0026     1     1     1
3.4800   3.4820   -.0020    -1     0     2
3.4300   3.4388   -.0088     0    -2     1
3.1000   3.1001   -.0001     1     0     2
3.0100   3.0109   -.0009    -2     1     1
2.9200   2.9237   -.0037    -1     2     0
2.8600   2.8552    .0048     2     1     1

A=  8.72858   DA= .00005
B=  6.96087   DB= .00002
C=  7.84219   DC= .00003
GAMMA= 82.1153   DGAMMA= .0001
BETA =101.7201   DBETA = .0001
ALPHA=113.5679   DALPHA= .0001
V=426.8

431. 37-1560
C7H4O3Zn
Triklin

  Dexp    Dcal     d(D)     h     k     l    
12.1100 12.1232  -.0132     1     0     0    
6.9600  6.9640  -.0040     0     1     0    
6.0400  6.0371   .0029    -1     1     1    
5.3700  5.3691   .0009     1     1     1    
4.0600  4.0578   .0022     2     0     1    
3.6300  3.6311  -.0011     1     2     1    
3.5000  3.5004  -.0004    -2     1     2    
3.3800  3.3783   .0017    -3     1     0    
3.1000  3.1012  -.0012     2    -1     1    
3.0000  3.0002  -.0002     1     2     2    
2.9030  2.9035  -.0005    -4     1     1    
2.6220  2.6219   .0001     3    -1     1    
2.4030  2.4028   .0002    -2     2     3    
2.3150  2.3148   .0002     1     3     0    

A= 12.443  DA= .001
B=  7.743  DB= .001
C=  7.5945 DC= .0006
GAMMA= 91.12 DGAMMA= .01
BETA =102.184 DBETA = .009
ALPHA= 64.478 DALPHA= .006
V=     643.3

432. 37-1881
C4.5H15Cl2N3Zn
Triklin

 Dexp    Dcal     d(D)     h     k     l    
8.8000  8.7978   .0022     1     0     0    
5.7000  5.6967   .0033     0     1     1    
5.2900  5.2898   .0002     0    -1     1    
4.8400  4.8388   .0012    -1     1     1    
4.5600  4.5694  -.0094     1     0     2    
4.2600  4.2567   .0033    -1     1     2     
3.8600  3.8577   .0023     2     0     1    
3.5300  3.5257   .0043    -2     1     1   
3.4200  3.4208  -.0008    -2     1     0   
3.2900  3.2872   .0028     0    -1     3   
2.9300  2.9326  -.0026     3     0     0   
2.6700  2.6687   .0013     0    -1     4   

A=  9.1029 DA= .0009
B=  6.1530 DB= .0005
C= 12.847  DC= .003
GAMMA= 85.80 DGAMMA= .02
BETA =103.90 DBETA = .01
ALPHA= 85.83 DALPHA= .02
V=     693.6

433. 38-0220
ZnSn{PO4}2*2H2O
Rombik
Groupa 19

Dexp.   Dcal.    d(D)      h    k    l
11.8100 11.7262   .0838      1    0    1
7.9200  7.9072   .0128      2    0    0
4.2200  4.2114   .0086      1    0    4
3.4900  3.4953  -.0053      0    0    5
3.1100  3.1123  -.0023      5    0    1
2.7800  2.7796   .0004      5    0    3
2.4800  2.4781   .0019      1    1    0
2.3900  2.3915  -.0015      2    1    0
1.9600  1.9597   .0003      5    0    7
1.5700  1.5699   .0001      9    0    5
1.2700  1.2700  -.0000      7    1    9

a=15.814  b= 2.509  c=17.477
da= .002  db= .001  dc= .001
V= 693.5

434. 38-0301
AgZnPO4
Triklin
 
 Dexp     Dcal      d(D)     h     k     l
4.7100   4.7188   -.0088     2     0     1
4.4400   4.4408   -.0008     0    -1     2
4.4200   4.4178    .0022    -2     1     0
4.3600   4.3607   -.0007     2     1     0
3.8900   3.8871    .0029    -2     2     0
3.7320   3.7318    .0002     2    -1     2
3.2380   3.2343    .0037     2     3     0
3.0910   3.0880    .0030     2     3     2
2.9960   2.9973   -.0013     3     1     0
2.9170   2.9157    .0013     1    -2     3
2.7430   2.7449   -.0019     2     4     0
2.5760   2.5762   -.0002    -2     3     2

A=  9.638  DA= .002
B= 13.921  DB= .001
C= 10.1257 DC= .0003
GAMMA= 89.720 DGAMMA= .003
BETA = 73.8359 DBETA = .0005
ALPHA= 84.704 DALPHA= .008
V=1299.2

435. 38-0302
Ag3Zn6{PO4}5
Triklin

 Dexp     Dcal      d(D)     h     k     l
6.4600   6.4624   -.0024    -1     1     1
6.0900   6.0876    .0024     2     0     0
5.1900   5.1890    .0010     0     2     0
4.7000   4.7032   -.0032     0     1     2
4.4000   4.4010   -.0010     0     2     1
4.2800   4.2779    .0021    -2    -2     1
4.1400   4.1402   -.0002     1     1     2
4.1000   4.1023   -.0023    -2     1     2
3.8500   3.8491    .0009    -2    -1     3
3.7700   3.7692    .0008    -2     0     3
3.7230   3.7240   -.0010    -3     1     1
3.7230   3.7240   -.0010    -3     1     1

A= 12.6388   DA= .0003
B= 10.7048   DB= .0002
C= 12.5981   DC= .0001
GAMMA= 84.341 DGAMMA= .001
BETA =105.437 DBETA = .001
ALPHA=104.04820   DALPHA= .00005
V=1593.0

436. 38-1775
C8H4O4Zn*2H2O
Monoklin   
Grupa  7,13

Dexp      Dcal       d(D)      h    k    l
8.5881    8.5782     .0099      0    1    1
6.1508    6.1476     .0032      2    0    0
4.9829    4.9876    -.0047      1    1    2
4.7200    4.7200     .0000     -2    0    2
4.2705    4.2731    -.0026      2    0    2
4.0953    4.0984    -.0031      3    0    0
3.7856    3.7868    -.0012      0    3    0
3.4663    3.4660     .0003     -3    1    2
3.4141    3.4148    -.0007      2    2    2
3.2090    3.2067     .0023     -1    3    2
2.9689    2.9671     .0018      4    1    0
2.8400    2.8401    -.0001      0    4    0

a= 12.3562 b= 11.3605 c=13.1490 beta= 95.694
da=.0007 db=.0009 dc=.0006 dbet=.003
V=    1836.6

Triklin

 Dexp     Dcal      d(D)     h     k     l
8.5881   8.6083   -.0202     0     1     0
6.1508   6.1513   -.0005     0    -1     2
4.9829   4.9838   -.0009    -2     0     1
4.7200   4.7226   -.0026     2    -1     1
4.2705   4.2698    .0007     2    -1     2
4.0953   4.0931    .0022    -2     0     2
3.7856   3.7859   -.0003     0     2     1
3.4663   3.4667   -.0004    -2    -2     1
3.4141   3.4142   -.0001     2    -2     2
3.2090   3.2100   -.0010     0     2     2
2.9689   2.9687    .0002    -2    -2     3
2.8400   2.8399    .0001     2     2     2

A= 11.16164   DA= .00001
B=  8.98193   DB= .00007
C= 13.81057   DC= .00003
GAMMA= 90.6767 DGAMMA= .0002
BETA = 85.38691   DBETA = .00002
ALPHA=106.5788 DALPHA= .0003
V=1322.62

437. 38-1776
C8H4O4Zn*1.5H2O
Triklin

  Dexp    Dcal     d(D)     h     k     l    
14.1910 14.1771   .0139     1     0     0    
7.0811  7.0854  -.0043     0     1     1    
5.3724  5.3773  -.0049     0    -1     1    
4.7200  4.7221  -.0021     1     2     0     
4.0953  4.0958  -.0005    -2    -1     1    
3.8338  3.8341  -.0003     2     1     2    
3.7385  3.7352   .0033     3    -1     1    
3.6776  3.6777  -.0001     2     0     2    
3.2204  3.2201   .0003    -2    -2     1    
3.1535  3.1530   .0005     2    -1     2    
3.0379  3.0373   .0006     2     3     0    
2.9402  2.9409  -.0007     3     3     1    

A= 14.517   DA= .001
B= 10.285   DB= .005
C=  8.190   DC= .002
GAMMA= 83.49 DGAMMA= .01
BETA = 78.00 DBETA = .01
ALPHA= 72.97 DALPHA= .01
V=    1141.8

438. 38-1777
C8H4O4Zn*3,5H2O
Triklin

 Dexp     Dcal      d(D)     h     k     l
7.4996   7.5127   -.0131     0     1     0
5.9535   5.9531    .0004    -1     0     1
5.3724   5.3682    .0042     2     0     0
5.2461   5.2493   -.0032    -1    -1     1
4.7959   4.7924    .0035     1    -1     1
4.5754   4.5811   -.0057     2     1     0
4.3323   4.3319    .0004     1     1     1
4.1521   4.1536   -.0015     2     0     1
3.6927   3.6963   -.0036     2    -1     1
3.2434   3.2421    .0013    -3     0     1
3.2434   3.2421    .0013    -3     0     1
2.8847   2.8845    .0002     3    -1     1

A= 10.80989   DA= .00004
B=  7.6949   DB= .0006
C=  7.080  DC= .001
GAMMA= 83.866 DGAMMA= .004
BETA = 93.783 DBETA = .006
ALPHA=101.24  DALPHA= .02
V=573.5

439. 38-1809
C10H7Cl2N3SZn
Monoklin
Grupa  4,11

Dexp      Dcal       d(D)      h    k    l
11.3000   11.2825     .0175      1    0    0
7.0500    7.0527    -.0027      0    1    1
6.2600    6.2536     .0064      1    0    1
5.6620    5.6412     .0208      2    0    0
4.7250    4.7289    -.0039      0    2    1
4.5840    4.5836     .0004      0    0    2
4.2640    4.2659    -.0019      2    0    1
4.1400    4.1384     .0016      1    2    1
3.9140    3.9176    -.0036     -3    0    1
3.3040    3.3038     .0002     -3    1    2

a= 11.830 b= 11.0400 c= 9.612 beta=107.495
da= .001 db=.0007 dc=.001 dbet=.002
V=    1197.2

Triklin

Dexp    Dcal     d(D)     h     k     l    
11.3000 11.2887   .0113     1     0     0    
7.0500  7.0502  -.0002     0     1     1    
6.2600  6.2624  -.0024     1     0     1    
5.6620  5.6626  -.0006     0    -1     1    
4.7250  4.7246   .0004    -2     1     0    
4.5840  4.5832   .0008     0     0     2    
4.2640  4.2639   .0001     0     2     0    
4.1400  4.1402  -.0002    -2     1     2    
3.9140  3.9140   .0000    -3     0     1    
3.3040  3.3041  -.0001     1    -1     2    

A= 11.8599  DA= .0001
B=  8.761  DB= .002
C=  9.863  DC= .002
GAMMA= 94.470  DGAMMA= .001
BETA =107.86  DBETA = .01
ALPHA= 76.76 DALPHA= .02
V=     949.56

440. 38-1816
C14H24N2S4Zn
Rombik
Groupa 19
 
  Dexp.   Dcal.    d(D)      h    k    l
 7.7890  7.8409  -.0519      1    0    1
 6.2540  6.2279   .0261      0    0    3
 4.8050  4.8044   .0006      0    1    1
 4.6550  4.6709  -.0159      0    0    4
 4.3180  4.3192  -.0012      2    0    0
 4.1970  4.1987  -.0017      1    1    1
 3.9140  3.9127   .0013      1    1    2
 3.7350  3.7368  -.0018      0    0    5
 3.4370  3.4296   .0074      1    0    5
 3.1670  3.1671  -.0001      1    1    4
 2.9280  2.9294  -.0014      1    0    6
 2.8460  2.8459   .0001      3    0    1
 
  a= 8.638  b= 4.972  c=18.684
  da= .001  db= .003  dc= .005
  V= 802.4

Triklin

 Dexp    Dcal     d(D)     h     k     l    
7.7890  7.7733   .0157     0     0     1    
6.2540  6.2486   .0054    -1     0     1    
4.8050  4.8045   .0005     0    -2     1    
4.6550  4.6585  -.0035    -1     2     0    
4.3180  4.3212  -.0032     1    -2     1    
4.1970  4.1957   .0013     0    -1     2    
3.9140  3.9138   .0002    -1    -1     2    
3.7350  3.7344   .0006    -1     2     1    
3.4370  3.4380  -.0010    -1     1     2    
3.1670  3.1670   .0000     0     1     2    
2.9280  2.9282  -.0002    -2    -1     2    
2.8460  2.8454   .0006    -2     3     0    

A=  7.52578   DA= .00004
B= 10.245  DB= .002
C=  8.613  DC= .002
GAMMA=106.08 DGAMMA= .01
BETA =102.71 DBETA = .01
ALPHA=107.1632 DALPHA= .0001
V=     575.9

441. 38-1843
C8H25Cl5CrN5Zn
Triklin

Dexp     Dcal      d(D)     h     k     l
7.2484   7.2594   -.0110     0     1     1
6.5532   6.5826   -.0294     1     1     1
5.6396   5.6221    .0175     0    -1     1
5.2417   5.2399    .0018     0     0     2
5.1509   5.1542   -.0033    -1    -1     1
4.6186   4.6288   -.0102    -1     1     0
4.4577   4.4544    .0033    -1     1     1
4.1872   4.1831    .0041     1     2     0
4.0367   4.0407   -.0040     0     2     1
3.8801   3.8824   -.0023     1     2     2
3.7509   3.7516   -.0007     2     0     0
3.7509   3.7516   -.0007     2     0     0

A=  8.1859   DA= .0008
B=  8.8721   DB= .0001
C= 10.9805   DC= .0005
GAMMA= 66.529 DGAMMA= .002
BETA = 81.331 DBETA = .002
ALPHA= 72.764 DALPHA= .002
V=698.2

442. 39-0079
Zn3{PO4}2*4H2O
Triklin

Dexp    Dcal     d(D)     h     k     l    
9.3000  9.2990   .0010     1     0     0    
5.3700  5.3716  -.0016    -1     1     1    
5.1500  5.1490   .0010    -1    -1     1    
4.9200  4.9187   .0013    -2     1     0    
4.6400  4.6403  -.0003     0     0     2    
4.4300  4.4295   .0005     2     0     1    
4.0400  4.0394   .0006     0     2     1    
3.4700  3.4688   .0012    -2    -1     1   
3.4200  3.4205  -.0005    -2     2     1    
3.1800  3.1803  -.0003    -3     2     0    
2.8800  2.8799   .0001    -2    -2     1    
2.5500  2.5504  -.0004     0    -4     2   

A= 10.281  DA= .002
B= 11.615  DB= .001
C= 10.00788   DC= .00007
GAMMA=113.852 DGAMMA= .001
BETA = 74.46  DBETA = .02
ALPHA=110.327 DALPHA= .001
V=    1013.7

 

443. 39-0080
Zn3{PO4}2*4H2O
Monoklin
Grupa 4,11

Dexp      Dcal       d(D)      h    k    l
10.5200   10.5030     .0170      1    0    0
9.8200    9.8251    -.0051      0    0    1
5.1800    5.1466     .0334      1    2    0
4.6400    4.6356     .0044     -2    0    2
3.6700    3.6857    -.0157      1    3    0
3.5000    3.5010    -.0010      3    0    0
2.8700    2.8639     .0061      0    2    3
2.5500    2.5495     .0005     -3    0    4
2.3000    2.3015    -.0015     -4    3    1
2.1600    2.1606    -.0006     -1    5    2
2.1400    2.1398     .0002     -3    3    4
1.9500    1.9515    -.0015     -5    3    1

a= 11.4704 b= 11.8080 c= 10.730 beta= 113.6951
da=.0007 db=.0006 dc=.001 dbet= .0008
V=    1330.7

444. 39-0347
Li9Zn6{PO4}7
Triklin

 Dexp     Dcal      d(D)     h     k     l
5.0570   5.0646   -.0076     2     0     0
4.0370   4.0360    .0010    -2     2     0
3.9730   3.9742   -.0012     2     1     1
3.7040   3.7037    .0003     2    -1     2
3.5410   3.5409    .0001     1     1     2
3.3480   3.3430    .0050    -2    -1     1
3.3170   3.3164    .0006    -1     3     0
3.1220   3.1232   -.0012     0    -2     2
2.7700   2.7693    .0007    -2    -2     1
2.6630   2.6646   -.0016    -1    -3     1
2.6540   2.6538    .0002     4    -2     1
2.5650   2.5662   -.0012    -2    -1     2

A= 11.0191 DA= .0008
B= 10.0724 DB= .0007
C=  8.2301 DC= .0004
GAMMA=106.248 DGAMMA= .002
BETA = 71.731 DBETA = .007
ALPHA= 98.061 DALPHA= .007
V=831.4

445. 39-0392
LiZn4{PO4}3
Triklin

 Dexp     Dcal      d(D)     h     k     l
7.6310   7.6116    .0194     0    -1     1
5.0010   4.9942    .0068     2     0     0
4.4110   4.4099    .0011     0     2     0
4.2530   4.2483    .0047     2     2     0
4.0610   4.0575    .0035    -2    -2     1
4.0090   4.0032    .0058     1     0     2
3.9180   3.9164    .0016     0     0     2
3.7990   3.8010   -.0020    -2     0     1
3.6280   3.6277    .0003     3     1     0
3.5420   3.5434   -.0014     2     0     2
3.2430   3.2432   -.0002    -2    -3     1
3.1910   3.1905    .0005     2     1     2

A= 10.9457  DA= .0001
B= 10.26246   DB= .00000
C=  8.6387   DC= .0003
GAMMA= 70.5092 DGAMMA= .0002
BETA = 84.006 DBETA = .003
ALPHA=110.513 DALPHA= .002
V=829.3

446. 39-0626
alfa-Zn{clO4}2
Rombik
Groupa  17

Dexp.   Dcal.    d(D)      h    k    l
7.3080  7.2793   .0287      0    1    0
4.1110  4.1036   .0074      1    1    0
3.6850  3.6902  -.0052      1    0    2
2.8380  2.8372   .0008      1    2    1
2.4120  2.4098   .0022      1    0    4
2.2910  2.2937  -.0027      1    2    3
2.0110  2.0093   .0017      1    2    4
1.7100  1.7088   .0012      1    4    0
1.5740  1.5747  -.0007      0    0    7
1.4520  1.4523  -.0003      1    4    4
1.3940  1.3946  -.0006      3    2    3
1.3670  1.3679  -.0009      3    3    0

a= 4.968  b= 7.279  c=11.02
da= .007  db= .005  dc= .01
V= 398.6

447. 39-0627
beta-Zn{ClO4}2
Triklin

  Dexp     Dcal      d(D)     h     k     l
5.9010   5.9008    .0002     1     1     0
5.5010   5.5026   -.0016    -1     1     1
4.7320   4.7331   -.0011    -1    -1     1
3.8640   3.8567    .0073    -2     1     1
3.7990   3.7964    .0026     1    -1     1
3.5590   3.5619   -.0029     0     0     2
3.2070   3.2078   -.0008    -2     1     2
3.0490   3.0500   -.0010    -1     2     2
2.8830   2.8819    .0011    -2    -1     2
2.8330   2.8340   -.0010     1    -2     1
2.8330   2.8340   -.0010     1    -2     1
2.7050   2.7049    .0001    -3    -1     1

A=  8.7498  DA= .0002
B=  8.2068  DB= .0009
C=  7.6878  DC= .0002
GAMMA= 91.271 DGAMMA= .009
BETA =108.760 DBETA = .003
ALPHA= 78.356 DALPHA= .001
V=511.2

448. 39-0628
RbZn{clO4}3
Triklin

 Dexp     Dcal      d(D)     h     k     l
8.8200   8.8383   -.0183     1     0     0
6.1460   6.1493   -.0033    -1     1     0
4.2830   4.2846   -.0016     1    -1     2
4.2110   4.2077    .0033     0     0     2
3.9520   3.9517    .0003     0    -1     2
3.8500   3.8522   -.0022     0    -2     1
3.7670   3.7645    .0025    -1     2     0
3.5480   3.5488   -.0008     0     1     2
3.2900   3.2924   -.0024     2     1     2
3.1490   3.1516   -.0026    -2    -1     1
3.0890   3.0891   -.0001     3    -1     1
3.0040   3.0035    .0005     1    -1     3

A=  9.649 DA= .003
B=  8.2286 DB= .0002
C=  9.2519 DC= .0009
GAMMA= 96.76 DGAMMA= .05
BETA = 66.56 DBETA = .02
ALPHA= 99.57 DALPHA= .03
V=662.9

449. 39-0638
MgZn2Br6*6H2O
Triklin

 Dexp    Dcal     d(D)     h     k     l    
7.3100  7.3046   .0054     1     0     0    
6.3300  6.3282   .0018     0     1     1    
5.2200  5.2240  -.0040     0    -1     1    
4.0100  4.0080   .0020    -1     2     1    
3.6700  3.6700  -.0000     1     2     1    
3.5100  3.5096   .0004     0     1     2    
3.3000  3.2980   .0020     2     0     1   
3.1600  3.1600  -.0000     1     1     2    
2.7060  2.7070  -.0010     2     2     1   
2.6130  2.6120   .0010     0    -2     2   
2.5840  2.5862  -.0022    -1     3     2   
2.5340  2.5340  -.0000    -2     1     2   

A=  7.381 DA= .001
B= 10.2424 DB= .0005
C=  7.100  DC= .001
GAMMA= 97.821 DGAMMA= .001
BETA = 88.918 DBETA = .005
ALPHA= 78.635 DALPHA= .002
V=     520.8

450. 39-0639
MnZnBr4*6H2O
Triklin

Dexp     Dcal      d(D)     h     k     l
6.4900   6.4809    .0091     0     0     1
5.4500   5.4585   -.0085     0    -2     1
4.9100   4.9124   -.0024     1     0     0
4.6800   4.6814   -.0014    -1     1     0
4.5300   4.5326   -.0026     1     2     0
4.1100   4.1076    .0024     1    -1     1
3.9500   3.9485    .0015     0    -4     1
3.5000   3.4992    .0008    -1    -2     1
3.3400   3.3438   -.0038    -1     4     0
3.2700   3.2668    .0032     0     6     0
3.1300   3.1298    .0002     1    -4     1
2.8200   2.8215   -.0015     1     6     0

A=  4.9875 DA= .0003
B= 19.659  DB= .001
C=  6.562  DC= .003
GAMMA= 85.76 DGAMMA= .01
BETA = 81.057 DBETA = .001
ALPHA= 90.52 DALPHA= .01
V=634.0

451. 39-0640
CaZn2Br6*6H2
Triklin

Dexp     Dcal      d(D)     h     k     l
8.1100   8.2304   -.1204     1     0     1
7.8300   7.8361   -.0061     0     1     0
5.7900   5.7983   -.0083     0    -1     2
5.3700   5.3762   -.0062    -1    -1     1
4.8500   4.8541   -.0041    -1     0     3
4.4600   4.4547    .0053    -2     0     1
4.1900   4.1970   -.0070    -2     1     0
4.1100   4.1152   -.0052     2     0     2
3.5700   3.5722   -.0022     0     2     2
3.4200   3.4183    .0017    -1    -1     4
3.4000   3.3992    .0008    -1    -2     1
3.2100   3.2127   -.0027    -1    -2     2

A=  9.325  DA= .001
B=  7.88468   DB= .00008
C= 17.293   DC= .005
GAMMA= 96.37 DGAMMA= .01
BETA = 88.96 DBETA = .03
ALPHA= 89.971 DALPHA= .003
V=1262.8

452. 39-0708
ZnHPO4
Monoklin
Grupa  14

Dexp      Dcal       d(D)      h    k    l
5.8960    5.9040    -.0080      1    1    0
4.0000    3.9990     .0010      1    1    2
3.8830    3.8793     .0037     -2    0    2
3.1590    3.1589     .0001      3    1    0
2.7100    2.7101    -.0001      3    1    2
2.6440    2.6440     .0000      4    0    0
2.5740    2.5742    -.0002      0    1    4
2.4550    2.4538     .0012     -3    2    1
2.3590    2.3567     .0023      4    0    2
2.3150    2.3145     .0005      1    3    0
2.1400    2.1397     .0003     -1    3    2
2.0490    2.0499    -.0009      3    2    3

a= 10.5810 b= 7.116 c=11.0500 beta= 91.753
da=.0009 db=.001 dc=.0003 dbet=.005
V=     831.6

Triklin

 Dexp     Dcal      d(D)     h     k     l
5.8960   5.8985   -.0025    -1     1     1
4.0000   3.9983    .0017     0    -1     1
3.8830   3.8856   -.0026     1    -1     1
3.1590   3.1554    .0036    -1    -1     1
2.7100   2.7107   -.0007    -2     3     1
2.6440   2.6467   -.0027     1     2     1
2.5740   2.5738    .0002     0    -1     2
2.4550   2.4557   -.0007    -2     3     0
2.3590   2.3578    .0012    -2    -1     1
2.3150   2.3163   -.0013    -1    -1     2
2.1400   2.1395    .0005     3     0     1
2.0490   2.0518   -.0028     1    -3     1

A=  8.064  DA= .005
B=  8.318  DB= .002
C=  7.134  DC= .004
GAMMA=120.52 DGAMMA= .04
BETA =104.98 DBETA = .02
ALPHA= 64.89 DALPHA= .02
V=372.9

453. 39-0711
Zn2P2O7
Triklin

 Dexp    Dcal     d(D)     h     k     l    
6.1720  6.1714   .0006     1     0     0    
5.1850  5.1837   .0013    -1     1     1    
4.9350  4.9397  -.0047    -1    -1     1    
4.6410  4.6458  -.0048    -1     2     0    
4.2400  4.2381   .0019     1    -1     1    
3.9730  3.9770  -.0040     1     0     1    
3.5440  3.5366   .0074     0     0     2   
3.3140  3.3140  -.0000    -2     0     1    
3.2350  3.2344   .0006    -2     1     0    
3.0820  3.0819   .0001     0     1     2    
2.8510  2.8499   .0011    -2     1     2    
2.7650  2.7665  -.0015    -2    -1     2   

A=  6.8131 DA= .0004
B= 10.7578 DB= .0005
C=  7.752  DC= .002
GAMMA=102.78 DGAMMA= .01
BETA =108.30 DBETA = .02
ALPHA=100.759 DALPHA= .003
V=     505.6

454. 39-0951
Mg32{Al,Zn}49
Rombik
Groupa 34,58
 
 Dexp.   Dcal.    d(D)      h    k    l
4.2300  4.2221   .0079      1    2    0
3.7400  3.7394   .0006      2    1    0
2.4230  2.4227   .0003      0    0    2
2.2920  2.2896   .0024      3    1    1
2.1290  2.1272   .0018      1    4    1
2.0320  2.0333  -.0013      2    1    2
1.7780  1.7786  -.0006      2    5    0
1.4280  1.4280   .0000      1    3    3
1.3510  1.3515  -.0005      3    6    1
1.2240  1.2239   .0001      1    8    0
1.2170  1.2169   .0001      3    6    2

a= 8.076  b= 9.905  c= 4.84537
da= .007  db= .003  dc= .0009
V= 387.6

4555. 39-1517
C18H16N2O6Zn*4H2O
Rombik
Groupa 31,59

Dexp.   Dcal.    d(D)      h    k    l
9.8255  9.8246   .0009      1    0    1
7.0811  7.0700   .0111      1    1    0
6.3256  6.3395  -.0139      2    0    0
4.7958  4.7958  -.0000      1    0    3
4.2302  4.2263   .0039      3    0    0
3.7855  3.7858  -.0003      3    1    0

a=12.679  b= 8.517  c=15.542
da= .001  db= .001  dc= .001
v=1678.4

456. 39-1695
C8H16N10O6S4Zn
Triklin

 Dexp     Dcal      d(D)     h     k     l
8.7677   8.7635    .0042     0     1     1
8.4019   8.4301   -.0282    -1     1     1
7.4057   7.4093   -.0036     0    -1     1
6.9751   6.9805   -.0054     2     0     0
6.8673   6.8559    .0114    -1     0     2
6.3655   6.3698   -.0043    -1     1     2
6.2668   6.2766   -.0098    -2     1     1
5.3550   5.3494    .0056     2     1     0
5.0691   5.0676    .0015    -1    -1     2
4.9401   4.9340    .0061    -1     2     1
4.8701   4.8753   -.0052     0     2     0
4.7160   4.7197   -.0037    -3     0     1

A= 14.5003  DA= .0003
B= 10.065   DB= .001
C= 14.647   DC= .003
GAMMA=100.16 DGAMMA= .01
BETA =103.770 DBETA = .003
ALPHA= 77.80  DALPHA= .04
V=2008

457. 39-1931
C49H49N2O9.5S3.5Zn
Rombik
Groupa  16,25,47

Dexp.   Dcal.    d(D)      h    k    l
13.0400 13.2409  -.2009      0    1    0
6.5800  6.6205  -.0405      0    2    0
4.4000  4.4136  -.0136      0    3    0
4.2200  4.2136   .0064      0    1    1
3.9600  3.9507   .0093      1    0    0
3.3900  3.3926  -.0026      1    2    0
3.3100  3.3102  -.0002      0    4    0
2.8800  2.8820  -.0020      1    1    1
2.6500  2.6482   .0018      0    5    0

a= 3.951  b=13.24  c= 4.445
da= .001  db= .02  dc= .007
V= 232.5

458. 39-1952
C16H14O4Zn*2H2O
Triklin

Dexp     Dcal      d(D)     h     k     l
12.8100  12.8803   -.0703     0     0     1
6.4170   6.4113    .0057     0     1     0
5.9860   5.9989   -.0129     2     0     1
5.6090   5.5725    .0365     1     1     1
5.1260   5.1393   -.0133    -2     0     1
4.8220   4.8293   -.0073     2     1     0
4.4840   4.4921   -.0081     1     1     2
4.2910   4.2934   -.0024     0     0     3
4.0580   4.0658   -.0078     2     1     2
3.7860   3.7843    .0017     2    -1     2
3.6780   3.6791   -.0011    -3     0     1
3.6190   3.6161    .0029     1    -1     3

A= 12.608 DA= .007
B=  6.5027 DB= .0003
C= 13.153  DC= .002
GAMMA= 81.365 DGAMMA= .005
BETA = 79.10 DBETA = .02
ALPHA= 92.49 DALPHA= .01
V=1045

459. 39-1953
C16H14O6Zn*2H2O
Triklin

  Dexp     Dcal      d(D)     h     k     l
13.1920  13.1917    .0003     1     0     0
11.6320  11.6391   -.0071     0     1     0
10.5260  10.5540   -.0280    -1     0     1
8.8450   8.8445    .0005     1    -1     1
8.1920   8.1791    .0129    -1    -1     1
7.5000   7.5015   -.0015    -1     1     1
6.5110   6.5118   -.0008    -1    -1     2
6.1510   6.1619   -.0109     0    -2     1
5.7540   5.7505    .0035    -1     2     0
5.4710   5.4824   -.0114    -2    -1     1
5.2780   5.2770    .0010    -2     0     2
4.9830   4.9809    .0021     1     2     0

A= 13.48810   DA= .00009
B= 12.50708   DB= .00001
C= 15.5856   DC= .0004
GAMMA= 99.0604 DGAMMA= .0003
BETA = 94.58818   DBETA = .00007
ALPHA=108.4810  DALPHA= .0007
V=2440.0

460. 39-1954
C14H8Cl2O4Zn*3H2O
Triklin

   Dexp     Dcal     d(D)     h     k     l    
12.6270 12.6418 -.0148     1     0     0    
6.3710  6.3795  -.0085     1    -1     0   
5.9460  5.9437   .0023     1     0     1    
4.9830  4.9778   .0052     1     1     1    
4.7960  4.8002  -.0042    -2     1     0    
4.2300  4.2301  -.0001    -1    -1     1    
3.7860  3.7801   .0059     2    -1     1    
3.6480  3.6482  -.0002     3     0     1    
3.2090  3.2091  -.0001    -3     1     1    
3.1540  3.1526   .0014     0     1     2    
3.0280  3.0281  -.0001    -3    -1     1   
2.9030  2.9037  -.0007    -4     1     0   

A= 12.6707  DA= .0006
B=  7.484   DB= .002
C=  6.588   DC= .002
GAMMA= 89.28  DGAMMA= .01
BETA = 86.14  DBETA = .01
ALPHA= 81.47  DALPHA= .01
V=     616.4

461. 39-1955
C14H8N2O8Zn*1.5H2O
Triklin

Dexp     Dcal      d(D)     h     k     l
12.4500  12.3113   .1387     1     0     0
9.7180   9.7179    .0001     0     1     0
7.9750   7.9629    .0121     0    -1     1
6.6569   6.6382    .0187     1     0     1
5.8288   5.8170    .0118     0     1     1
5.5050   5.5085   -.0035     2     1     0
4.7200   4.7177    .0023     1     2     0
4.1908   4.1868    .0040    -3    -1     1
3.9515   3.9549   -.0034     3     1     0
3.7078   3.7097   -.0019     0     1     2
3.4663   3.4660    .0003    -1    -3     1
3.2784   3.2796   -.0012    -2    -3     1

A= 12.907   DA= .004
B= 10.4217  DB= .0006
C=  9.945  DC= .007
GAMMA= 78.252  DGAMMA= .009
BETA =106.0973  DBETA = .0006
ALPHA=110.07   DALPHA= .01
V=1201.5

462. 39-1956
C14H8N2O8Zn*3.5H2O
Triklin

   Dexp      Dcal      d(D)     h     k     l
18.9620  18.9602   .0018     1     0     0
18.8000  18.7997   .0003     0     1     0
8.3457   8.3422    .0035     0     1     1
6.7071   6.7032    .0039     0     2     1
6.1936   6.1947   -.0011    -2    -1     1
5.8288   5.8266    .0022     2     1     1
4.6953   4.6961   -.0008     3     1     1
4.4838   4.4828    .0010    -2     4     0
4.1521   4.1535   -.0014     3     3     0
3.9002   3.9007   -.0005     1    -2     2
3.7231   3.7232   -.0001    -2    -2     2
3.4796   3.4801   -.0005    -5     3     0

A= 19.2833   DA= .0004
B= 19.0514   DB= .0005
C=  9.14036   DC= .00009
GAMMA= 98.86   DGAMMA= .01
BETA = 96.201  DBETA = .004
ALPHA= 86.16  DALPHA= .05
V=3294

463. 39-1957
C14H8N2O8Zn*5H2O
Triklin

   Dexp    Dcal      d(D)     h     k     l    
12.6270 12.6267  .0003     1     0     0    
6.3256  6.3134   .0122     2     0     0    
5.2155  5.2148   .0007     0     1     1    
4.6465  4.6458   .0007     0    -1     1    
4.2104  4.2101   .0003     2     0     1    
3.5758  3.5743   .0015     0     2     1    
3.2090  3.2088   .0002     1    -2     1    
3.0583  3.0591  -.0008    -1     1     2    
2.9497  2.9521  -.0024     3     1     1   
2.6070  2.6074  -.0004     0     2     2    
2.5425  2.5435  -.0010    -4    -1     1   
2.2594  2.2591   .0003     5     0     1    

A= 13.100   DA= .001
B=  8.3693  DB= .0008
C=  6.2879  DC= .0004
GAMMA=104.343 DGAMMA= .003
BETA = 97.703  DBETA = .001
ALPHA= 81.527  DALPHA= .009
V=     657.22

 
 
-
 
-